CompositesImpact resistantChemical resistantStrongFunctional

SLS Nylon PA11 Carbon Fiber

PA11-CF is a very rigid material thanks to its carbon fiber reinforcement, which makes it a perfect option for applications where rigidity really matters. It is also the perfect choice for lightweight designs without compromising a part's functionality, which can be interesting to manufacture, for example, some motorsport parts.

Print with SLS Nylon PA11 Carbon Fiber

Mechanical Properties

Tensile strength65–85 MPa

Tensile modulus5000–6500 MPa

Elongation3–7 %

Flexural strength90–120 MPa

Flexural modulus5000–6000 MPa

Density1.09 g/cm³

Thermal

Heat deflection at 66 PSI

Available finishes

Each finish can be combined with the available colors at checkout.

Standard

1 color

SLS Nylon infused with Carbon fiber results in slightly coarse surface.

Polished

1 color

SLS nylon PA 11 infused with carbon fiber and with a polished smooth surface.

All materials

Print Constraints

Maximum build volume

350 × 350 × 360 mm

Default layer height0.15 mm

Default infill100%

Min embossing0.3 mm

Min engraving0.3 mm

Accuracy± 0.3 mm

Warping riskModerate

Interlocking partsSupported

SLS Nylon PA11 Carbon Fiber

Available finishes

Standard

Polished

Vapor Smoothed