HP® Carbon Fiber Nylon

Composites

StrongDurableFunctionalImpact resistant

Nylon reinforced with short carbon fibers offers properties close to what is usually achievable only by injection molding. Excellent mechanical properties and smooth appearance make it ideal for demanding automotive structural applications that require robust performance at elevated temperatures.

Print with HP® Carbon Fiber Nylon

Mechanical Properties

Tensile strength66–110 MPa

Tensile modulus6000–8100 MPa

Elongation3–10 %

Flexural strength127–140 MPa

Flexural modulus4300–6500 MPa

Density1.52 g/cm³

Thermal

Heat deflection at 66 PSI150–190 °C

Print Constraints

Maximum build volume

365 × 365 × 415 mm

Default layer height0.25 mm

Default infill20%

Min embossing0.8 mm

Min engraving0.8 mm

Accuracy± 0.4 mm

Warping riskLow

Interlocking partsSupported