Glass Fiber ULTEM 1010

Glass Fiber ULTEM 1010

Composites
Chemical resistantHeat resistantStrongFlame retardant

Glass-fiber reinforced ULTEM 1010 PEI (Polyetherimide) is a high-performance thermoplastic composite known for its outstanding strength, thermal stability, and chemical resistance. The addition of glass fibers to ULTEM 1010 enhances its mechanical properties, including increased stiffness, dimensional stability, and improved strength-to-weight ratio. This material retains its properties over a wide temperature range and exhibits excellent flame retardancy and low smoke emission, making it suitable for aerospace, automotive, and electrical/electronic applications. Its superior strength and rigidity, combined with inherent PEI characteristics, make it ideal for advanced engineering applications where durability and performance in harsh environments are essential.

Print with Glass Fiber ULTEM 1010
Mechanical Properties
Tensile strength58–145 MPa
Tensile modulus4300–8790 MPa
Elongation2–3 %
Flexural strength53–178 MPa
Flexural modulus4299–8560 MPa
Density1.51 g/cm³
Thermal
Heat deflection at 66 PSI206–212 °C
Print Constraints

Maximum build volume

300 × 300 × 400 mm

Default layer height0.2 mm
Default infill20%
Min embossing0.5 mm
Min engraving0.5 mm
Accuracy± 0.3 mm
Warping riskOver_140_mm
Interlocking partsSupported

Available finishes

Each finish can be combined with the available colors at checkout.

Standard

Standard

1 color

Standard layered finish.

Sanded

Sanded

1 color

Smooth sanded finish.

All materials